ESAB

FILARC KV3L

FILARC KV3L

Application: All-position, basic-coated electrode with max. 0.05% C, for welding creep-resistant steels alloyed with 2.25Cr/1Mo, such as 10 Cr-Mo 9 10. Filarc KV3L is also recommended for welding 0.5Cr/0.5Mo/0.025V steels. The chemical composition of the weld metal guarantees low sensitivity to solidification cracking, as a result of Mn/Si control. A minimum preheating and interpass temperature of 165-190°C is recommended for all material thicknesses.

Agregar a la Lista de Compras


Especificaciones


Clasificaciones: SFA/AWS A5.5, E8015-B3L, EN ISO 3580-A, E CrMo2L B 2 2 H5
Aprobaciones: VdTÜV, Seproz, UNA 272581

Aprobaciones vinculadas a la planta de producción. Para obtener más información, pongase en contacto con ESAB.


Alloy Type: Low alloyed
Coating Type: Basic
Diffusible Hydrogen: < 5.0 ml/100g
Welding Current: DC+

Propiedades de Ensayo de impacto Charpy

ISO PWHT 690°C 1h
Testing Temperature
20 °C

Typical Tensile Properties

ISO PWHT 690°C 1h
AWS PWHT 690°C 1h

Datos aportación

Amperios Diámetro Fusion time per electrode at 90% I max kg weld metal/kg electrodes Number of electrodes/kg weld metal Tasa de Deposición Voltios
65-95 A 2.5 x 350 mm 63 sec 0.57 kg 76.9 0.7 kg/h 24 V
90-130 A 3.2 x 350 mm 70 sec 0.55 kg 50.0 1.0 kg/h 24 V
125-165 A 4.0 x 350 mm 80 sec 0.57 kg 34.5 1.3 kg/h 24 V