FILARC 98S


All-positional, low-hydrogen electrode for welding higher strength steels, depositing weld metal with a minimum yield strength of 550 N/mm2 after stress relieving.

Agregar a la Lista de Compras


Especificaciones


Propiedades tensoras típicas

PWHT 580°C 1h
Alargamiento Gas de protección Límite de elasticidad Resistencia a la tracción Stress Relieved Temperature Stress Relieved Testing Time
21 % ISO 650 MPa 710 MPa - -
Stress relieved
Alargamiento Gas de protección Límite de elasticidad Resistencia a la tracción Stress Relieved Temperature Stress Relieved Testing Time
- AWS - - 620 °C 1 hr

Propiedades de Ensayo de impacto Charpy

PWHT 580°C 1h
Gas de protección Temperatura de ensayo Valor de impacto
ISO -50 °C 80 J
ISO -60 °C 60 J

Análisis del Metal de Soldadura

MnMoCSiNiCr
1.85 %0.32 %0.06 %0.35 %0.89 %0.05 %

Datos aportación

Amperios Diámetro kg de metal de soldadura/kg de electrodos Número de electrodos/kg de metal de soldadura Tasa de Deposición Tiempo de fusión por electrodo al 90 % I máx. Voltios
55-85 A 2.5 x 350 mm 0.60 kg 83.3 0.72 kg/h 60 sec 24.4 V
80-140 A 3.2 x 350 mm 0.55 kg 56.6 0.94 kg/h 68 sec 23.3 V
120-180 A 4.0 x 450 mm 0.60 kg 24.4 1.43 kg/h 103 sec 24.0 V

Aprobaciones: ABS, E9018-G, NAKS/HAKC, 3.2 - 4.0 mm, Seproz, UNA 272581
Clasificaciones: SFA/AWS A5.5, E9018-G, EN ISO 18275-A, E 55 6 Mn1NiMo B T 32 H5

Aprobaciones vinculadas a la planta de producción. Para obtener más información, pongase en contacto con ESAB.


Corriente de soldadura: AC, DC+-
Hidrógeno difusible: < 5.0 ml/100g
Tipo de aleación: Low alloyed (0.9 % Ni, 0.3 % Mo)