Exaton 19.9.LR
Exaton 19.9.LR is a chromium-nickel covered electrode with acid rutile coating for welding of low carbon 18% Cr/10% Ni austenitic stainless steels. In cases where creep strength is of secondary importance Exaton 19.9.LR is suitable for welding stabilized austenitic steels, e.g. ASTM 321 and 347. When a weld metal similar to the parent metal is not required Exaton 19.9.LR can be used for welding ferritic and martensitic steels. The electrode has excellent arc stability, low spatter and fast burn off rate with minimal stub loss. It is also characterized by improved moisture resistance, self peeling slag, easy post weld finishing. Exaton 19.9.LR gives smooth uniform beads and works in any standard weld position.
Propiedades de Ensayo de impacto Charpy
| as welded iso | ||||
Propiedades tensoras típicas
| Alargamiento | Condición | Gas de protección | Límite de elasticidad | Resistencia a la tracción |
| 40 % | As Welded | ISO | 440 MPa (64 ksi) | 600 MPa (87 ksi) |
Datos aportación
| Amperios | Tasa de deposición al 90 % I máx. | Diámetro | Rendimiento (%) | Número de electrodos/kg de metal de soldadura | Voltios | |
| 50-90 A | 39 sec | 1.0 kg/h (2.2 lb/h) | 2.5 x 300.0 mm (0.098 x 11.8 in.) | 58 % | 94 | 28 V |
| 70-130 A | 54 sec | 1.4 kg/h (3.1 lb/h) | 3.2 x 350.0 mm (1/8 x 13.8 in.) | 60 % | 49 | 31 V |
| 90-180 A | 56 sec | 2.0 kg/h (4.4 lb/h) | 4.0 x 350.0 mm (5/32 x 13.8 in.) | 60 % | 33 | 32 V |
| 140-250 A | 60 sec | 2.8 kg/h (6.2 lb/h) | 5.0 x 350.0 mm (0.197 x 13.8 in.) | 60 % | 21 | 33 V |
Clasificaciones
| Clasificaciones |
EN ISO 3581-A : E 19 9 L R 1 2 SFA/AWS A5.4 : E308L-17 Werkstoffnummer : 1.4316 |
Aprobaciones
| Grado | EN 13479 |
| Sociedad | CE |
| Las aprobaciones dependen de la ubicación de la fábrica. Póngase en contacto con ESAB para obtener más información. |
Características de los consumibles
| Tipo de aleación | Austenitic CrNi |
| Tipo de recubrimiento | Acid Rutile |
| Contenido de ferrita | FN 3-10 |
| Corriente de soldadura | DC+, AC |
Análisis del Metal de Soldadura
| à% Análisis metal depositado (valores típicos) | ||||||||||||||
| C | Cr | Cu | FN WRC-92 | Mn | Mo | N | Ni | P | S | Si | ||||
| 0.025 % | 19 % | 0.04 % | 7 % | 0.75 % | 0.04 % | 0.062 % | 9.5 % | 0.024 % | 0.014 % | 0.9 % | ||||